銅材性質表格

material,E(kgf/mm^2),Yieldstress(kgf/mm^2),TensilStress(kgf/mm^2),min.R/t(badway/goodway),COFFICIENTOFTHERMALEXPANSION(cm/cm×10^-6/℃),THERMALCONDUCTIVITY(cal/cm-℃-sec),ELECTRICALCONDUCTIVITY(%IACS)

PHOSPHORBRONZE磷青銅,,,,,,,

JISC5210R-SH,11200,74.2,75~85,0.6,,0.16,13

JISC5210R-SH(預鍍材),11000,74Min,75～85,,,,10

JISC5210R-EH,11200,11Min,70～80,,18,67,13

JISC5210R-H,11200,,60～72,,,,13

C5211RH,11200,,60～72,,,,

JISC5191R-H,11200,64,60～70,Bendradius<=2.0mm,,,

JISC5191R-1/2H,,,49～61,,,,

C5191EH,11200,68,>=68,,,,14

C511R-EH,11260,53.0MIN,58.0～68.0,3.0/1.5,18,0.17,15Min.

C5111R-EH(B),11260,50.6MIN.,54.0~64.2(B),2/0.3,18,0.17,15

C510-SH,11250,64.7～76.0,66.8～77.4,,0.17,,15Min.

C510R-1/2H,,33～48,48～58,,,,20

C510-H,,51～62,53～64,,,,15

CDAC51000R-SH,11200REF,70Min,66.5~77,,,0.17,15

C510-H(904-0000-099),13500,80～95,98Min,,,,17

C5102WBD50WIRE,11700,,36.7/44.9,,,,16.4

C5102R-EH,11200,56Min,63～72,,,,15Min

JISH3110-C5111R-H,,,50~60,,18,0.17,21

CDAC51000R-SH,11200REF,70Min,66.5~77,,0.000178,0.17,15

"DIEHLMETAL,SundwigerMessingwerkC51100Alloy",1148(N/mm2),540Min(N/mm2),610MIN(N/mm2),,,,19

H3110-C5111R-H,50~60,,,,18,0.17,21

BRASS黃銅,,,,,,,

CDA2601/2H,,36.5,40～47,,,,

CDA260EH,,58REF,58～64,,,,

CDA260H,,,49.9-56.9,,,,29

JISC2680R-O,10500,,28Min,,,,

C2600-0,,,275Min,,20.3um/m.k,20℃,24～27.8

JISC2680R-EH,10500,47,53,,,,27

JISC2680R-SH,10500REF,60REF,58.0～68.0,,20.3um/m.k,116w/m.k,24～30

CDA160H:JISC2600-H,,23,49.9~56.9,,19×10-5,0.29,28

JISC2680R-H,,,42～55,,,,29

JISH3100C2680R-H(預鍍材),10500,47MIN,41~57,,,,27

JISH3100C2680R-1/2H,,,36~42,,,,

C36000,97000(Mpa),170Min(Mpa),395Min(Mpa),,20.5um/m.k,115w/m.k,

BERLLIUMCOPPER鈹銅,,,,,,,

ASTMB768,14100,56~71,67~81,0.5/0.5,18,0.55,50~60

"Alloy290TMO4,ASTM:C17200-HM,

JIS:172R-HM",,80~95,98.4min,,17.8,83.7~130(w/mk),25

CDAC17510-HM(BeCu板),13400,70Min,74～94,2,,,50Min

C17410-HT,14071AFTERAGING,70～84AFTERAGING,77.5~91.3,,,0.56,45～60

BRUSHWELLMANC17460-H,14074,73.5～87.8,84.2～98.5,1.5/1.5,,0.52(w/mk),50min

C17200-HM(ALLOY190-HM),13400,77～95,94～106,,,,17～28

JISC17200-SHM,13400,87~99,105~110,3.2/1.8,17.8,83.7~130,17~28

C17200-1/2H(ASTMB194-92A(TD02)),,52.5~66.5(75~95)kgf/mm2(KSI),59.5~70(85~100)kgf/mm2(KSI),,,,15~19

C17200-TM08(ALLOY290-TM08),13370,109～123,123MIN,,,,17～26

C17200-XHM(ALLOY190-XHM),13400,94~120,108~124,,,,17~28

C17200290TM(BRUSHWELLMAN),13400,80~95,98min,,,,17~26

C17530-HT,12959REF,70Min,78-92,0.7,,38,

COPPERALLOY銅合金,,,,,,,

SundwigerSB22,12960,59.1Min,63.2Min,1.0/0,17,,45Min

"SundwigerSB24,CuNiSiSn",13000,61,66～76,1.0/0,17,220(w/mk),38Min

SMWSTOL92R650,13000,58Min,65～80,4(BEND90°)/2(BEND90°),17,0.49,38Min

SMWSTOL92R650KX2876,13000,62Min,67~77,2.0/1.0,17,230(w/mk),Min.38

SMWSTOL92,13000,56Min,63Min,5(BEND90°)/2(BEND90°),17,0.49,45Min

SB31,11700,58Min,60~72,1.5,,,25MIN

OLINBRASSC7025TM02(ASTMB422),13700,59-77,67-84,2.0t/1.5t,,0.35-0.45,40

高性能銅合金,,,,,,,

日礦金屬C7025-TM03,13100,64.3～84.6,70.4～87.8,1/1.7,,,45Min

M702C-H,11000,60,60Min,2.0/1.3,17.3,195,47

"OLIN,C19025-EH",,53Min,55Min,2.0/1.5,,,40

OlinC197R-1/2H,12000,25Min,37~45,,,,80

OlinC197R-EH,12000,40.0Min,45~57,0.244,,,80

"COLDROLLEDSTAINLESSSTRIP冷軋不銹鋼帶(板)

",,,,,,,

JISSUS301-1/4H,"19,700",,75MIN,,"16.9/

18.7(0TO100℃/

0TO650℃",0.0388(w/mk),

JISSUS430-CS-H-2B,20400,,60Min,,"0～100℃:10.4

0～650℃:11.9",0.0624,

JISSUS304-CSP-H,19700,90MIN.,115MIN,,,,

JISSUS304-CS-3/4H,19700,,95～105,,"0～100℃:17.3

0～650℃:18.7",0.0388,

JISSUS304-CS-1/2H,19700,,71MIN,,"0～100℃:17.3

0～650℃:18.7",,

JISSUS301-CSP-3/4H,19700,76MIN,115Min,,16.9,0.0388,

鋁合金,,,,,,,

JISH4000A1050H14,,,9.5MIN,,,,

JISA1100-H14,95MIN,,110~145Mpa,,,,

JISA1100H16,350REF,13REF,13~17,,,218~222cal/cm-℃-sec,

"

ZINCALLOY鋅合金",,,,,,,

INTERNATIONLLEADZINERESEARCHORGANIXATION/DIN1743(Z430),,283Mpa,359Mpa,,27.8,,

JISH5301-1997(ZDC2),,,29min,,,0.27W/MK,82

鍍鋅鋼板,,,,,,,

JISG3313SECCT-P-10,,,28MIN,,,,

"鈦銅

TITANIUMCOPPER",,,,,,,

JISC199(TICUR1-M-EH),,,95~110,,95~110,,13

快削剛棒,,,,,,,

JISG4804SUM-24L,,,,,,,

REDBRASS,,,,,,,

ASTMB36,11.08~12.21.0E4N/mm2,,480(N),,,159(w/mk),37

鈹銅銅棒,,,,,,,

JISC17300H,,52～74,63～92,,,,15～19

JISG3141SPCC-SD,,,27.6Min,,,,

銅鎳合金,,,,,,,

"OLIN,C7025TM03",13000minREF,66~84REF,70~88,,,,35min

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,,,,,,,,

,