《利用水熱法來合成制備銅納米線試驗研究》6700字（論文）

十三參考文獻XieS,HouG,ChenP,etal.Applicationofmetalnanowirenetworksonhydrogenatedamorphoussiliconthinfilmsolarcells[J].Nanotechnology,2017,28(8):085402.JiangZ,TianY,DingS.Synthesisandcharacterizationofultra-longandpencil-likecoppernanowireswithapenta-twinnedstructurebyhydrothermalmethod[J].MaterialsLetters,2014,136(dec.1):310-313.孔德兵.銅納米線的液相法制備及生成機理研究[D].中北大學,2019.WangL,ChenH,ChenM.FacilesynthesisandcharacterizationofAu–Cu,Pt–Cunanotubesbysacrificialtemplatemethod[J].MaterialsResearchBulletin,2014,53(may):185-189.張穎.銅納米線的制備、特性及應用(下)[J].石油化工,v.38(10):1031-1037.WangZL.CharacterizingtheStructureandPropertiesofIndividualWire-LikeNanoentities[J].AdvancedMaterials,2000.GarnettE,YangP.Semiconductornanowiresforphotovoltaicandphotoelectronchemicalenergyconversion[J].NanoLetters,2010,10:1082-1085.FangZ,GengY,WangJ,etal.Mechanicalpropertiesofgoldnanowirespreparedbynanoskivingapproach[J].Nanoscale,2020,12(15).BinWU,BolandJJ,HeidelbergA.Mechanicalpropertiesofultrahigh-strengthgoldnanowires.[J].NatureMaterials,2005,4(7):525-9.EspinosaHD,BernalRA,MMinary‐Jolandan.AReviewofMechanicalandElectromechanicalPropertiesofPiezoelectricNanowires[J].AdvancedMaterials,2012,24(34).WangJ,SansozF,HuangJ,etal.Near-idealtheoreticalstrengthingoldnanowirescontainingangstromscaletwins[J].InternationalJournalofSurgeryCaseReports,2013,4:669-674.Atransformingmetalnanocompositewithexceptionalproperties[J].中國科學基金：英文版,2013(1期):19-19.YueY,LiuP,ZhangZ,etal.ApproachingtheTheoreticalElasticStrainLimitinCopperNanowires[J].NanoLetters,2011,11(8):3151.OsterlohF.Inorganicnanostructuresforphotoelectrochemicalandphotocatalyticwatersplitting[J].ChemicalSocietyReviews,2013,42(6):2294-2320.KoenigsmannC,SantulliAC,GongK,etal.Enhancedelectrocatalyticperformanceofprocessed,ultrathin,supportedPd-Ptcore-shellnanowirecatalystsfortheoxygenreductionreaction.[J].JournaloftheAmericanChemicalSociety,2011,133(25):9783-9795.ZhangY,GuoJ,XuD,etal.SynthesisofUltralongCopperNanowiresforHigh-PerformanceFlexibleTransparentConductiveElectrodes:TheEffectsofPolyhydricAlcohols[J].Langmuir,2018:acs.langmuir.8b00344.BerginSM,ChenYH,RathmellAR,etal.Theeffectofnanowirelengthanddiameteronthepropertiesoftransparent,conductingnanowirefilms[J].Nanoscale,2012,4(6):1996-2004.WuTong,BolongHuang,PengtangWang,QiShao,XiaoqingHuang.Exposedfacet-controlledN_2electroreductionondistinctPt_3Fenanostructuresofnanocubes,nanorodsandnanowires[J].NationalScienceReview,2021,8(01):117-126.HuangL,FanZ,LiX,etal.FacilesynthesisofCaFe2O4nanocubesforformaldehydesensor[J].MaterialsLetters,2021(5):129351.WangT,YangL,LiY,etal.SimpleandEfficientSynthesisofVariousSizedGoldNanoparticlesfortheSelectiveElectrochemicalDeterminationofDopamine[J].AnalyticalLetters,2020(16):1-17.Melinda,Mohl,Peter,etal.Low-TemperatureLarge-ScaleSynthesisandElectricalTestingofUltralongCopperNanowires[J].Langmuir,2010,26(21):16496–16502.WangY,LiuP,ZengB,etal.FacileSynthesisofUltralongandThinCopperNanowire