GB/T 44307-2024 是一項關(guān)于碳纖維增強(qiáng)塑料（Carbon Fiber Reinforced Plastic, CFRP）中纖維質(zhì)量含量測定方法的國家標(biāo)準(zhǔn)。該標(biāo)準(zhǔn)具體規(guī)定了利用熱重分析法（Thermogravimetric Analysis, TGA）來測定CFRP中碳纖維質(zhì)量比例的詳細(xì)操作規(guī)程和要求。以下是該標(biāo)準(zhǔn)的主要內(nèi)容概述：

  1. 適用范圍：本標(biāo)準(zhǔn)適用于各種碳纖維增強(qiáng)塑料材料，目的是準(zhǔn)確測定其中碳纖維的質(zhì)量含量，為CFRP材料的性能評估、質(zhì)量控制及產(chǎn)品研發(fā)提供科學(xué)依據(jù)。

  2. 術(shù)語和定義：標(biāo)準(zhǔn)首先明確了與測試相關(guān)的專業(yè)術(shù)語，如熱重分析、基線、失重率等，確保測試過程中的表述統(tǒng)一和明確。

  3. 原理：熱重分析法基于樣品在程序控制溫度下質(zhì)量變化的測量。通過加熱樣本，并連續(xù)監(jiān)測樣本因熱解或其他化學(xué)反應(yīng)導(dǎo)致的質(zhì)量減少，可以推算出碳纖維的質(zhì)量含量。此過程中，基體樹脂的分解可與碳纖維質(zhì)量穩(wěn)定的特點相區(qū)分，從而計算出纖維含量。

  4. 儀器要求：標(biāo)準(zhǔn)詳細(xì)描述了進(jìn)行熱重分析所需的儀器設(shè)備規(guī)格，包括但不限于精度、加熱速率控制、氣氛控制（如氮氣保護(hù)以避免氧化）等要求，以確保測試結(jié)果的準(zhǔn)確性與重復(fù)性。

  5. 樣品制備：規(guī)定了樣品切割、稱重、尺寸等制備步驟和條件，確保樣品代表性且能適配于熱重分析儀。

  6. 測試條件：包括初始溫度、最終溫度、升溫速率、氣氛類型（如惰性氣體環(huán)境）等參數(shù)設(shè)定，這些條件需根據(jù)CFRP的具體類型和研究目的適當(dāng)調(diào)整。

  7. 數(shù)據(jù)處理：說明了如何通過熱重曲線分析確定基體樹脂的失重區(qū)間，進(jìn)而計算碳纖維的質(zhì)量百分比。包括基線校正、扣除空白試驗的影響等數(shù)據(jù)處理方法。

  8. 精密度和準(zhǔn)確度：提供了重復(fù)性和再現(xiàn)性試驗的要求和評價方法，以驗證測試方法的可靠性和不同實驗室間結(jié)果的一致性。

  9. 試驗報告：規(guī)定了試驗報告應(yīng)包含的信息，如樣品描述、測試條件、觀察到的現(xiàn)象、計算過程及最終結(jié)果等，確保測試結(jié)果的完整記錄和可追溯性。


如需獲取更多詳盡信息，請直接參考下方經(jīng)官方授權(quán)發(fā)布的權(quán)威標(biāo)準(zhǔn)文檔。

....

查看全部

  • 即將實施
  • 暫未開始實施
  • 2024-08-23 頒布
  • 2025-03-01 實施
?正版授權(quán)
GB/T 44307-2024碳纖維增強(qiáng)塑料纖維質(zhì)量含量的測定熱重分析法(TG)_第1頁
GB/T 44307-2024碳纖維增強(qiáng)塑料纖維質(zhì)量含量的測定熱重分析法(TG)_第2頁
GB/T 44307-2024碳纖維增強(qiáng)塑料纖維質(zhì)量含量的測定熱重分析法(TG)_第3頁
GB/T 44307-2024碳纖維增強(qiáng)塑料纖維質(zhì)量含量的測定熱重分析法(TG)_第4頁
免費預(yù)覽已結(jié)束，剩余12頁可下載查看

下載本文檔

GB/T 44307-2024碳纖維增強(qiáng)塑料纖維質(zhì)量含量的測定熱重分析法(TG)-免費下載試讀頁

文檔簡介

ICS

59.100.20

CCS

Q53

中華人民共和國國家標(biāo)準(zhǔn)

GB/T44307—2024/ISO22821:2021

碳纖維增強(qiáng)塑料

纖維質(zhì)量含量的測定

熱重分析法（TG）

Carbon-fibre-reinforcedcomposites—

Determinationoffibreweightcontent—

Thermogravimetry(TG)

[ISO22821:2021，Carbon-fibre-reinforcedcomposites—

Determinationoffibreweightcontentbythermogravimetry(TG)，IDT]

2024-08-23發(fā)布2025-03-01實施

國家市場監(jiān)督管理總局發(fā)布

國家標(biāo)準(zhǔn)化管理委員會

GB/T44307—2024/ISO22821:2021

目次

前言

·····································································································

Ⅲ

1

范圍

··································································································

1

2

規(guī)范性引用文件

······················································································

1

3

術(shù)語和定義

···························································································

1

4

原理

··································································································

1

5

試劑

··································································································

1

6

儀器?熱重分析儀

·····················································································

2

7

試樣

··································································································

2

8

試驗步驟

······························································································

3

9

結(jié)果計算和表示

······················································································

3

10

精密度

·······························································································

4

11

試驗報告

····························································································

4

附錄A（資料性）熱重示例圖

········································································

5

附錄B（資料性）精度─可重復(fù)性

·································································

8

參考文獻(xiàn)

··································································································

9

Ⅰ

GB/T44307—2024/ISO22821:2021

前言

本文件按照GB/T1.1—2020《標(biāo)準(zhǔn)化工作導(dǎo)則第1部分：標(biāo)準(zhǔn)化文件的結(jié)構(gòu)和起草規(guī)則》的規(guī)定

起草。

本文件等同采用ISO22821:2021《碳纖維增強(qiáng)塑料用熱重分析法（TG）測定纖維質(zhì)量含量》。

本文件做了下列編輯性改動：

—為與現(xiàn)有標(biāo)準(zhǔn)協(xié)調(diào)，將標(biāo)準(zhǔn)名稱改為《碳纖維增強(qiáng)塑料纖維質(zhì)量含量的測定熱重分析

法（TG）》。

請注意本文件的某些內(nèi)容有可能涉及專利。本文件的發(fā)布機(jī)構(gòu)不承擔(dān)識別專利的責(zé)任。

本文件由全國碳纖維標(biāo)準(zhǔn)化技術(shù)委員會（SAC/TC572）提出并歸口。

本文件起草單位：南京玻璃纖維研究設(shè)計院有限公司、中復(fù)神鷹碳纖維股份有限公司、江蘇恒神股

份有限公司、中國石化上海石油化工股份有限公司、常州達(dá)姆斯檢測技術(shù)有限公司、上海飛機(jī)制造有限

公司、吉林化纖集團(tuán)有限責(zé)任公司、江蘇亨博復(fù)合材料有限公司、上海中鐳新材料科技有限公司。

本文件主要起草人：時慧嫻、李駿光、湯志強(qiáng)、金亮、胡瑋、韓風(fēng)、袁宇慧、王玉梅、張涵佳、

徐琪、孫攀、劉春艷、宋楠、鄭佩琪。

Ⅲ

GB/T44307—2024/ISO22821:2021

碳纖維增強(qiáng)塑料

纖維質(zhì)量含量的測定

熱重分析法（TG）

1范圍

本文件描述了一種用熱重分析法測定碳纖維增強(qiáng)復(fù)合材料纖維質(zhì)量含量的方法。

本文件適用于碳纖維預(yù)浸料和碳纖維增強(qiáng)塑料。

2規(guī)范性引用文件

下列文件中的內(nèi)容通過文中的規(guī)范性引用而構(gòu)成本文件必不可少的條款。其中，注日期的引用文

件，僅該日期對應(yīng)的版本適用于本文件；不注日期的引用文件，其最新版本（包括所有的修改單）適用

于本文件。

ISO291塑料

試樣狀態(tài)調(diào)節(jié)和試驗的標(biāo)準(zhǔn)環(huán)境（Plastics—Standardatmospheres

for

condition?

ingandtesting）

注：GB/T2918—2018塑料試樣狀態(tài)調(diào)節(jié)和試驗的標(biāo)準(zhǔn)環(huán)境（ISO291:2008，MOD）

3術(shù)語和定義

下列術(shù)語和定義適用于本文件。

3.1

纖維質(zhì)量含量fibreweightcontent

Wf

纖維復(fù)合材料中纖維質(zhì)量與總質(zhì)量之比。

注：也稱纖維含量，以百分比表示。

4原理

在已知氣體環(huán)境中，按照預(yù)設(shè)程序?qū)ΨQ重的試樣進(jìn)行加熱。

先將試樣在惰性氣體環(huán)境（氮氣）中進(jìn)行初始熱解，然后在氧化性氣體中燃燒。

一般來說，產(chǎn)生質(zhì)量變化的反應(yīng)有分解、氧化或反應(yīng)揮發(fā)等。

繪制質(zhì)量損失與溫度的熱重函數(shù)關(guān)系圖，對預(yù)浸料或復(fù)合材料的碳纖維含

溫馨提示

  • 1. 本站所提供的標(biāo)準(zhǔn)文本僅供個人學(xué)習(xí)、研究之用，未經(jīng)授權(quán)，嚴(yán)禁復(fù)制、發(fā)行、匯編、翻譯或網(wǎng)絡(luò)傳播等，侵權(quán)必究。
  • 2. 本站所提供的標(biāo)準(zhǔn)均為PDF格式電子版文本（可閱讀打?。?，因數(shù)字商品的特殊性，一經(jīng)售出，不提供退換貨服務(wù)。
  • 3. 標(biāo)準(zhǔn)文檔要求電子版與印刷版保持一致，所以下載的文檔中可能包含空白頁，非文檔質(zhì)量問題。

評論

0/150

提交評論